Jump to content

Bent forth wheel pivot - what do you do?

Stian

By Stian
in Watch Repairs Help & Advice

 Share

Recommended Posts

Stian WRT Addict

Stian

Posted
Posted

Hi guys, 

I working on a watch with small seconds, and the extended pivot on the fourth wheel is a bit bent. I would assess it to be maybe 3 or 4 degrees bent. This is enough for the seconds hand to rotate on a tilted plane, and the dial had been marked by it. 

Do you try to straighten the pivot, and if so, how? 

--

Thanks, 

Stian 

Link to comment
Share on other sites
Stian WRT Addict

Stian

Posted
  • Author
Posted

Hi Stuart, 

Thanks, I should have specified that this is a vintage watch and finding a new arbor would be very difficult. 

Would you have any guidance on when you would expect it to break and when you would think you can straighten it? E.g would it depend on the angle, the method etc? 

Stian 

Link to comment
Share on other sites
StuartBaker104 Distinguished Member

StuartBaker104

Posted
Posted

Hi Stian,

It is more likely to break if you can't find a replacement :-)

On older watches, the hardness of these parts is somewhat unpredictable. Seitz makes a special tool for straightening pivots, but they are expensive even second hand.  This would give you more control, but wouldn't help with certainty.

If it is only a few degrees you may get away with it. Do you have a staking set with hollow punches?

If you post some pictures we may be able to help identify the movement. Key features are usually the keyless works parts and the diameter, but also good to see the bridges and any markings

 

Link to comment
Share on other sites
jdrichard Distinguished Member

jdrichard

Posted
Posted

I had the same problem and was successful in straightening it out. I used a pair of pliers and carefully worked it. Then I used my Jacot tool to smooth out any scratches I made with the pliers. As mentioned by others, the pivot could break if you are not careful and even if you are. However, you really have no choice other than getting a new wheel and shaft.

Sent from my GT-N5110 using Tapatalk

Link to comment
Share on other sites
matabog Super WRT Addict

matabog

Posted
Posted

Never done it myself, but from what I heard, if you want to work with the pivot (in any way) you must first soften the material (meaning turning it red, letting it cool down) and then hardening it again.

Good luck with that!

 

 

Link to comment
Share on other sites
praezis Super WRT Addict

praezis

Posted
Posted

@ matabog: Oh god, do not heat to red! Light blue is sufficient.

If it is bent 3-4 deg only, danger of breaking is not so high. I do this very often, repairing chronographs. I use to hold the pivot (the straight part) in a lathe collet, turn the spindle and compare the other pivot to the tip of the headstock. Bend the pivot with light taps until the wheel wobbles no more.

Frank

 

 

 

Link to comment
Share on other sites
anilv Distinguished Member

anilv

Posted
Posted

General answer.

1st step (hardening). Heat red hot and quench in oil.

2nd step (tempering). Heat but not red hot. straw is the usually quoted  colour , then quench again.

The problem is these processes work on larger items where the piece heats up gradually. A small part like a pivot will heat up red-hot practically instantly. You would need to set up a bed of copper shavings and heat this part on it but it pretty hit and miss. There are some good videos on hardening watch parts on youtube.

A replacement would be the way to go.

Anilv

 

Link to comment
Share on other sites
StuartBaker104 Distinguished Member

StuartBaker104

Posted
Posted

I came across this thread whilst researching re-pivoting earlier. http://mb.nawcc.org/showthread.php?118580-Escape-wheel-pivot-repair

The idea of letting down the temper slightly might appeal. I'm no expert in this, but suspect that re-tempering the whole pinion with wheel attached is going to cause you bigger issues than you have already.

Link to comment
Share on other sites
praezis Super WRT Addict

praezis

Posted
Posted
 

I came across this thread whilst researching re-pivoting earlier. http://mb.nawcc.org/showthread.php?118580-Escape-wheel-pivot-repair

The idea of letting down the temper slightly might appeal. I'm no expert in this, but suspect that re-tempering the whole pinion with wheel attached is going to cause you bigger issues than you have already.

You are right. I do not heat at all, but reducing the temper to blue or light blue may help. Tempering again is not needed.

Frank

Link to comment
Share on other sites
 Share
Go to topic listing


  • Recently Browsing

    • No registered users viewing this page.

  • Topics

  • Posts

    • Bonefixer
      Pocket watch escape wh

      By Bonefixer · Posted

      The wheels turned fine. I set the escape wheel in the epoxy when it had just ‘skinned’ and wasn’t set, made sure it spun with the 4th wheel, and let it set.    After cleaning I assembled the barrel and wheel train - all fine. Moving the barrel the escape wheel spun freely. I put a bit of 9010 in my epoxy setting.    It went wrong when I put the pallet fork in. It wasn’t seated right (no jewels) and the escape wheel  knocked a pallet jewel out. I have no idea how to reset a pallet jewel - epoxy again? I’m not spending any more time on this one - it’s missing hands and the front half of the case anyway, and I have more watches ready to put on the bench. 
    • RichardHarris123
      Without Our Forum

      By RichardHarris123 · Posted

      No John, we don't want Mark to change anything, we are just scared of losing a brilliant forum and losing contact with each other.  As pointed out, this forum is full of knowledge and I for one,  consider the regulars friends. I would hate to lose contact with you and the others.   PS, this forum is really important to me. 
    • JohnR725
      Epilame / Fixodrop

      By JohnR725 · Posted

      one little minor problem with your chemistry experiment here which is what exactly is epilam? In other words is it an exact substance with the chemical you specify or is it a term? For instance originally it was steric acid either dissolved in some sort of solvent or it was applied by vaporizing it. Then now it's all kinds of different things the watch companies all have different ideas there's a whole bunch of patents. So is not always an exact substance.   let me snip out a image from the patent that I attached up above. Notice I highlighted something it seems to disagree with your evaluation.  
    • nevenbekriev
      Pocket watch escape wh

      By nevenbekriev · Posted

      I guess You had to try, as it would be hard to sleep without that try, but, I know the result before the experiment... As I told before, the friction will be so big that the wheel will not turn. The pivots have to be thin and polished - the bigger the number of the wheel (2th, 3gh, 4th...), the thinner the pivot. What You are trying to do is possible, but forming the new thin pivot must be done on lathe. Thus the wheel will get shorter, but can have new pivot without the drilling for normal standard repivoting. Then piece of brass can be soldered under the pivot hole in the bridge and new hole drilled in it to form the new bearing.  Well, this way is not the recommended one, not quite correct, but it is possible to do for the excersize... When I say lathe, lathe may be verry simple, someting like turns, but made of what one has in reach of his hands. If You want to try, I will try to guide
    • JohnR725
      Without Our Forum

      By JohnR725 · Posted

      yes by all means let's gather up our weapons tar feathers find the nearest tree in case Mark is not agreeable to our terms on our demands and storm his Castle. I don't quite understand what you're trying to do here? In other words you want Mark to somehow guarantee that the group will live on forever no matter what? You want Mark to somehow change his business model of what is trying to do or should we just take the group away from him? oh and is quite possible that Mark never realized that his discussion group would take on a life of its own. That the members of the group would like to continue on forever.  
×
×
  • Create New...