Re-Luming An Old Radium Dial To Restore Radio-Luminescence.

cdjswiss
 Share

Recommended Posts

cdjswiss WRT Addict

cdjswiss

Posted
Posted

Roland Ranfft is offering two re-luming pastes with excellent instructions on their use (as in Mark's video). One is based on the phosphor Zinc Sulphide (ZnS) , the other on Luminova.

http://www.ranfft.de/cgi-bin/bidfun.cgi?10&ranfft&b7&1usem&1456959600
http://www.ranfft.de/cgi-bin/bidfun.cgi?10&ranfft&b7&1usem&1456959601

These will glow for a few hours after exposure to sunlight (phosphorescence).

The early Radium luminous dials and hands glowed continuously due to the very long lifetime Alpha and Beta emission. Today an early Radium dial has no more radio-luminescence due to radiation damage to the phosphor (usually silver activated ZnS). But a dial with a good coating of old luminous paint (see below) can be brought to life again by applying a new overlay of ZnS.
I asked Ranfft to test this out and he found that non-activated ZnS applied over an old radio-luminous dial did glow even after several hours in the dark when the light-activated phosphorescence would have vanished. He also reported that Luminova was also activated in the same way but with more brightness than the ZnS.

Our conclusion is that if you have a radio-luminescent dial in good condition such as this one


post-374-0-89407700-1425839975_thumb.jpg

Then it could be brought to life again to glow all night long by the application of a layer of Luminova paste over the old numbers and hands. Silver activated ZnS paste would also perform well and be nearer to the original. Activated ZnS is available in small quantities from:

https://unitednuclear.com/index.php?main_page=product_info&cPath=16_17_69&products_id=218

If you do want to get into this game then buy a cheap (post Fukushima) radiation monitor from one of the Japanese eBay sources.
The above dial has a radiation dose rate above the crystal of 40 micro Sv/h. This is ample for a re-luming job.
 

  • Like 2
Link to comment
Share on other sites
bobm12 Distinguished Member

bobm12

Posted
Posted

Hi Colin,

 

Good to know! I'm planning on re-luming some stuff but I need to practice first on some hands in order to get it down pat before I attempt a dial. I'm saving the links for future use!

 

Cheers,

 

Bob

Link to comment
Share on other sites
cdjswiss WRT Addict

cdjswiss

Posted
  • Author
Posted

That's an enlightening post Colin, thanks for sharing. Are you going to re-activate the old Rolex lume?

Not until I have tried it out on this old Tudor Oyster that is even hotter at 65 micro Sv/h.

 

post-374-0-28766000-1425884748.jpg

 

I also wonder if it is only the hands of the Rolex that are active - the dial looks too good to be original.

Link to comment
Share on other sites
bobm12 Distinguished Member

bobm12

Posted
Posted (edited)

I'll also be interested in the how-to of the whole thing. It seems like a super precise job: one little blink and the dial can go bye-bye! Also, Colin, be careful with the radioactive material. You never know with those, sometimes even a small amount could be a real hazard.

 

Cheers,

 

Bob

Edited by bobm12
Link to comment
Share on other sites
  • 7 months later...
Arny Member

Arny

Posted
Posted

Thanks for the info

But

https://unitednuclea...products_id=218

On the LINK these people state that this stuff can be shipped anywhere,

BUT

First before you can purchase you have to be a member, you spend valuable time filling in

this ridiculous form with an address outside of the USA & Canada

It's then & only then they inform you that they only ship within the USA & Canada.

I have set a curse upon their webmaster

"I HOPE ALL HIS TEETH FALL OUT EXCEPT F­OR ONE, WHICH SHOULD REMAIN NONE REMOVA­BLE IN

ORDER TO GIVE Him SEVERE TOOTHACHE FOR THE REST OF HIS LI­FE. "

How do I load Pics?

Kind Regards

Tony (Arny)

Link to comment
Share on other sites
Arny Member

Arny

Posted
Posted (edited)

I'm trying to edit my last post in order to remove my address, but I keep receiving this message (see pic)

HELP

After all its my post so surely I should be able to edit

Many Thanks in advance

Kind Regards

Tony

post-344-0-03055400-1444721798_thumb.jpe

Edited by Arny
Link to comment
Share on other sites
  • 3 months later...
cdjswiss WRT Addict

cdjswiss

Posted
  • Author
Posted

Thanks for bringing this post to life again with this link to Unitednuclear fluorescent paints. These are really no different than the others such as Luminova or the ones sold by Ranfft.

 

This is a point I still do not grasp: are all luming pastes, even the new ones, radioactive? Are the ones Ranfft sells radioactive?

 

Sorry George to be so late with a reply. The only radioactivity in everything that has been mentioned in this post is the very old residual radium paint on the dial and hands of vintage watches. The radium is still active but not the fluorescent material that was destroyed long ago by the radiation..

 

If a thin layer of  paint such as Luminova is applied over the old dial numbers or hands then it will glow because of the radium underneath, and this glow will be permanent lasting longer than the short-lived glow from exposure to light or ultra-violet rays (sunshine). This short-lived glow is phosphorescence caused by light, whereas the radium induced glow is usually called fluorescence.

 

In Tritium fluorescent watches (marked with a T on the dial) the radioactivity is from the Tritium gas that is contained together with the fluorescent material in glass micro-spheres. The radioactivity emitted by Tritium is low energy (penetrating power) and so it does not pass through the glass. If the glass spheres are ground down by accident the Tritium gas would just fly away presenting no hazard.

  • Like 2
Link to comment
Share on other sites
  • 4 years later...
  • 2 years later...

Join the conversation

You can post now and register later. If you have an account, sign in now to post with your account.
Note: Your post will require moderator approval before it will be visible.

Guest
Reply to this topic...

×   Pasted as rich text.   Restore formatting

  Only 75 emoji are allowed.

×   Your link has been automatically embedded.   Display as a link instead

×   Your previous content has been restored.   Clear editor

×   You cannot paste images directly. Upload or insert images from URL.

×
 Share
Go to topic listing


  • Recently Browsing

    • No registered users viewing this page.

  • Topics

  • Posts

    • RichardHarris123
      Without Our Forum

      By RichardHarris123 · Posted

      No John, we don't want Mark to change anything, we are just scared of losing a brilliant forum and losing contact with each other.  As pointed out, this forum is full of knowledge and I for one,  consider the regulars friends. I would hate to lose contact with you and the others.   PS, this forum is really important to me. 
    • JohnR725
      Epilame / Fixodrop

      By JohnR725 · Posted

      one little minor problem with your chemistry experiment here which is what exactly is epilam? In other words is it an exact substance with the chemical you specify or is it a term? For instance originally it was steric acid either dissolved in some sort of solvent or it was applied by vaporizing it. Then now it's all kinds of different things the watch companies all have different ideas there's a whole bunch of patents. So is not always an exact substance.   let me snip out a image from the patent that I attached up above. Notice I highlighted something it seems to disagree with your evaluation.  
    • nevenbekriev
      Pocket watch escape wh

      By nevenbekriev · Posted

      I guess You had to try, as it would be hard to sleep without that try, but, I know the result before the experiment... As I told before, the friction will be so big that the wheel will not turn. The pivots have to be thin and polished - the bigger the number of the wheel (2th, 3gh, 4th...), the thinner the pivot. What You are trying to do is possible, but forming the new thin pivot must be done on lathe. Thus the wheel will get shorter, but can have new pivot without the drilling for normal standard repivoting. Then piece of brass can be soldered under the pivot hole in the bridge and new hole drilled in it to form the new bearing.  Well, this way is not the recommended one, not quite correct, but it is possible to do for the excersize... When I say lathe, lathe may be verry simple, someting like turns, but made of what one has in reach of his hands. If You want to try, I will try to guide
    • JohnR725
      Without Our Forum

      By JohnR725 · Posted

      yes by all means let's gather up our weapons tar feathers find the nearest tree in case Mark is not agreeable to our terms on our demands and storm his Castle. I don't quite understand what you're trying to do here? In other words you want Mark to somehow guarantee that the group will live on forever no matter what? You want Mark to somehow change his business model of what is trying to do or should we just take the group away from him? oh and is quite possible that Mark never realized that his discussion group would take on a life of its own. That the members of the group would like to continue on forever.  
    • RichardHarris123
      Second hand watch market.

      By RichardHarris123 · Posted

      I'm not sentimental, I see it this way.  I inherit something I  don't like, I could sell it, buy something I do like and remember the person with the new item.  For example, I  inherit a watch ( I haven't), I don't like it, I  buy a watch I do like, every time I look at the watch, I think of the person. 
×
×
  • Create New...