About 5 years ago, before I got into clock repair, we had our grandfather clock serviced (It had not worked for a few years) I was moving the clock over the weekend so thought I would have a look at the movement just see what it was like only to find, what looks to me, to be some dubious bushing! see the pictures and let me know your thoughts.

On work that I do I try and keep it as original and tidy as I can. I've not re-bushed a long case clock before but I would expect the principals to be the same. 

Grandfather Clock (2).jpg

Grandfather Clock (1).jpg

Link to comment
Share on other sites

Hi Roger  the obvious thing is the bushings are very visible and stand proud of the countersink so oiling the bush would be almost useless as it would not be retained on the pivot. No oil well , I would have expected them to turned down to the original plate depth  and be almost invisible. What are they like on the inside.(flush with the plate?)

Link to comment
Share on other sites

Hi Watchweasol, they actually look ok although there's not a lot of end shake on some of them - tbf, I didn't get too involved but one day I'll get it on the bench for a proper look. To me it just lacked a bit of care or thought. as you say, they should be pretty much invisible! One more for my to do list.

Link to comment
Share on other sites

Shocking repairs. First the crutch has had a blob of solder on it to hold it in place. The bushing is all wrong, wrong colour brass, no care in matching to the plate so they stick out like a sore thumb. Wrong depth so no oil wells. Seeing the pivots I would say the wrong type of bush have been used. I would love to see the condition of the plate from the inside. 

Link to comment
Share on other sites

We don't have a "before" picture, so perhaps not fair to judge every fault on the most recent overhaul. On less valuable clocks, and in particular where the movement is not visible, I think the aesthetics matter less. And then there is the amount paid for the work. Doing work with a fine finish takes a lot of time.

It may be simple to tidy up the existing bushes.

Link to comment
Share on other sites

Join the conversation

You can post now and register later. If you have an account, sign in now to post with your account.
Note: Your post will require moderator approval before it will be visible.

Guest
Reply to this topic...

×   Pasted as rich text.   Restore formatting

  Only 75 emoji are allowed.

×   Your link has been automatically embedded.   Display as a link instead

×   Your previous content has been restored.   Clear editor

×   You cannot paste images directly. Upload or insert images from URL.



  • Recently Browsing

    • No registered users viewing this page.
  • Topics

  • Posts

    • I did that also for a few movements - well, mainly in/around the train jewels. I made big efforts to epilame the mainplate WITHOUT getting Epilame into the Pallet fork jewels (where it's not supposed to be, right?). I made litte barriers with Rodico around that jewel and used drops from a syringe to apply on the rest.  However, I've now stopped doing this. For three reasons: 1. It's a hassle and consumes more of this liquid gold. 2. I didn't see the need when using HP1000/HP1300 lubricants and grease for most part. The two places where I'd use 9010 (i.e. escape wheel and balance) receive Epilame in specific places... or the cap-jewel-setting of the balance suspends the oil sufficiently be capillary action (see my "conflict" about using Epilame on the balance jewels).  3. Lastly, and here I really wonder about yours and others' experiences: I felt that applying Epliame to the train jewels left them looking hazy (borderline dirty) compared to the (painstakingly achieved) sparkly clean results of my cleaning process. I just can't help but think that the Epilame residuals would mix with the oil and cause more friction/wear. I don't know.    simple: it'll stay there. It won't move any further. That's exactly what is happening if you epilame a cap stone. You end up placing the 9010 right on top of the epilame and the oil will sit nicely on that spot.
    • There are some parts on Ebay for the seiko 6020A, it may just be a waiting game for someone to strip one down, NOS will be more scarce . K would strip your movement down to the module then start looking at other seiko movement to see if that coil is used, then seek out a seiko part dealer. Also Retrowatches youtube owner Mike may give you some advice try him on his site . He also hangs around amateur watchmaking groups.
    • I would agree, in order to work harden something you need to exceed it's yield strength when it moves from the elastic zone to the plastic zone and you get permanent deformation and work hardening which is fairly close to its failure point, relatively speaking and dependent on the material/alloy of course. In theory you can load something constantly within its elastic range and not suffer work hardening issues.
    • Probably easier to get a complete new movement - but CousinsUK list it as discontinued. Maybe someone on here knows a substitute movement ?
    • Any other thoughts on how I can get a replacement coil? Any “hidden” or unknown physical shops (in Australia or elsewhere) that might have them in stock (but not always online)?
×
×