A very fine sand is needed for a fine, frosted finish. Probably a 50 micron or 25 micron sand.

If you have a dental lab in your city, they might do it for you if you ask them very nicely. But you'll probably need to mask the areas you don't want frosted yourself.

Link to comment
Share on other sites
  • 1 month later...
JohnFrum WRT Addict

JohnFrum

Posted
Posted

Another option would be places that do custom vehicle rims. They have bead blasting equipment.  I had a watch bracelet bead blasted a few years ago. The guy didn’t even charge.  Much smaller object than they normally deal with. As Hector says, you will have to mask out (kapton tape) the areas you need to protect. 
 

Link to comment
Share on other sites

Join the conversation

You can post now and register later. If you have an account, sign in now to post with your account.
Note: Your post will require moderator approval before it will be visible.

Guest
Reply to this topic...

×   Pasted as rich text.   Restore formatting

  Only 75 emoji are allowed.

×   Your link has been automatically embedded.   Display as a link instead

×   Your previous content has been restored.   Clear editor

×   You cannot paste images directly. Upload or insert images from URL.

×
 Share
Go to topic listing


  • Recently Browsing

    • No registered users viewing this page.

  • Topics

  • Posts

    • ManSkirtBrew
      Seitz Tool - Help determine if Seitz or not

      By ManSkirtBrew · Posted

      Right now I'm making do with a similar micrometer (the one below is $45 shipped but you can find better deals) and a $20 stand. You do have to be excruciatingly careful measuring jewels, since there's no table, but if you don't have the $500 to throw around, it's a nice option.
    • noirrac1j
      Watch of Today

      By noirrac1j · Posted

      As  I kid, I'd watch Godzilla stomping over buildings and cars and I'd think to myself: Tokyo is a really dangerous place to live... . Cool watch!!
    • Neverenoughwatches
      Part swapper to part maker

      By Neverenoughwatches · Posted

      Next one up an AS 554, looks like a bit more to this one. First job is to check thickness, most springs are somewhere between .3 and .4, this one measures .35, that matches in with the .4 spring steel i ordered. So for marking up a permanent marker comes in handy to colour up the steel to be marked later with a scriber once its dry. Bestfit provide the extra bit of info for the jumper spring that is missing.
    • Hawaiikook808
      Seitz Tool - Help determine if Seitz or not

      By Hawaiikook808 · Posted

      Thanks again, Marc.  Super helpful. I was wondering what the hole was for, and now it makes perfect sense. With your help and the other members here, it looks like I'm good to go with my Seitz tool set. I had to order some replacement pushers, but with those, the set is complete and in good condition. Now, I need to figure out what tool to buy to measure jewels (amongst other watch-related parts). I had my eye on the JKA Feintaster micrometers, but people get crazy bidding on them for $400-600 USD. I was thinking of just a regular digital micrometer (Mitutoyo). Thoughts?  Mahalo. Frank      
    • Marc
      Seitz Tool - Help determine if Seitz or not

      By Marc · Posted

      Yep, that's exactly how it should fit. The reamer shank is tapered and the socket in the spindle is also tapered so that the one centers in the other and is gripped tightly. If there is any wobble when the reamer is seated as far it will go then there is a problem. The cross hole in the spindle is to allow you the push the reamer back out again. If the reamer seated much deeper then it would limit the access for pushing it back out again. Here is one of mine for comparison.
×
×
  • Create New...