I am not really happy with this but it could have been worse.

This is a sweep second pinion that had a broken pivot.  I already found the replacement and really do not need this, but I thought it would be fun to try.

I started without doing any annealing.  Then realized that I needed to.  Just heated it over an alcohol burner.  I know there is an art to knowing when to stop...give me some time.

Also, failed to center properly.  Tomorrow, I will turn a pivot--needs to be 0.2mm.

I was thinking about @nickelsilverwhile I was doing this...knowing he could do it in minutes...likely with his eyes closed.

One thing I got from this was some confidence building (even though I broke the 0.1mm drill bit grrrrr).

2022-01-25 19_29_26-IMG_7896.JPG ‎- Photos.png

  • Like 1
Link to comment
Share on other sites
  • 1 month later...

Join the conversation

You can post now and register later. If you have an account, sign in now to post with your account.
Note: Your post will require moderator approval before it will be visible.

Guest
Reply to this topic...

×   Pasted as rich text.   Restore formatting

  Only 75 emoji are allowed.

×   Your link has been automatically embedded.   Display as a link instead

×   Your previous content has been restored.   Clear editor

×   You cannot paste images directly. Upload or insert images from URL.

×
 Share
Go to topic listing


  • Recently Browsing

    • No registered users viewing this page.

  • Topics

  • Posts

    • KarlvonKoln
      B-Dip residue?

      By KarlvonKoln · Posted

      One-dip or naphtha should be safe, but are you sure it isn't magnetized?  I would also check that.  Although, if that balance is from an Elgin 760 0r 761, I would think it would have a hairspring of non-magnetic alloy.
    • Curare
      Spell Check

      By Curare · Posted

      Hi, Is there a spell check function available when you are posting ? Regards CJ
    • Curare
      Replacing armoured crystal in a front loading watch case…

      By Curare · Posted

      Hi John I just did a Seiko Lord-Matic a front loader without a split stem, I used a crystal lift to remove it, although I had to have it that tight I though I was going to break the lift before the crystal would budge. So I decided that the press would be a better option as I think crystals with tension rings resist a lot of compressing. I used a crystal press to repalce it and the bezel with no issues, obviuosly a different watch to the Omega. I just took my time and kept inspecting the installation progress bit by bit Regards CJ
    • Zendoc
      Replacing armoured crystal in a front loading watch case…

      By Zendoc · Posted

      Hello All, I’m replacing the crystal in an Omega Dynamic, # 165.039, which houses a cal 552, installed through the front of the case. The replacement Sterncreuz crystal is, like the original, with tension ring. I removed the crystal using a compressed air technique to pop it out.  (I have a crystal lift, but I’m always fearful of marking the crystal edges and so avoid using it as much as possible). Now to the replacement -  any tips on putting the crystal back in?  Am I obliged to using my dreaded crystal lift to complete the task, or how about a crystal press?  I’ve put lots of crystals in using a press, but never with the movement in the watch. The thought of using one with a front-loader makes me very nervous, with the fully assembled watch sitting under the press. How would more experienced folks proceed here? Any advice, gratefully received… John Down Under…
    • Neverenoughwatches
      AS 554 from 1930

      By Neverenoughwatches · Posted

      No thats straight out of the watch as i found it the balance wheel is almost as bad. I've never seen so much material removed.
×
×
  • Create New...