Solid 18K Gold Lug Repair Advice


JBerry

Recommended Posts

Hey guys,

I picked up an old boxed Seiko Cronos in 18K solid gold from Japan,
I am absolutely delighted with it, however I noticed one of the lugs has a little bit of sideways play.
The bond between the lug and the case appears to be cracked, as I hope I've shown in the photos.
I'm wondering what the best way to go about this repair is, is there some kind of epoxy I could use to secure this? or is soldering/resetting the bond possible with a conventional soldering iron?

Thanks so much for the advice in advance, I know there is a lot of information available on soldering lugs online, but given that my lug is still in place, and is partially secured I hope there is a simpler solution.

IMG_6608.JPG

IMG_6609.JPG

IMG_6610.JPG

IMG_6604.JPG

IMG_6607.JPG

Link to comment
Share on other sites

  • 2 weeks later...

I went to a well recommended local jeweller...

He advised me in order to solder the lugs he would have to bring the case up to such a high temperature that it would likely warp the case.

Is there any truth in this? Before I went in he was confident he could fix it, but made this claim based on the shape of the case.

Link to comment
Share on other sites

He doesn’t want the job.

Technoflux cool paste is a heat insulation paste used to protect areas not requiring heat when soldering e.g. stones, areas of metal or solder joins. The paste is applied liberally to the area, heat is then applied (during soldering),

  • Thanks 1
Link to comment
Share on other sites

13 minutes ago, oldhippy said:

He doesn’t want the job.

 

Technoflux cool paste is a heat insulation paste used to protect areas not requiring heat when soldering e.g. stones, areas of metal or solder joins. The paste is applied liberally to the area, heat is then applied (during soldering),

 

Thanks again OH, that's a relief. Now to find someone that does want it... is there anyone in the UK you would personally recommend?, I would be content to post this off. Otherwise I can try a few more relatively local places and the NAJ list Mark sent.

Edited by JBerry
punctuation
Link to comment
Share on other sites

It could warp the case, though someone competent with a torch would have a low risk. Perhaps they've already gotten bit by picky watch folks in the past and just don't want the potential headache as OH said.

Many jewelers now can do laser welding but that won't be as strong as soldering on this job.

  • Thanks 1
Link to comment
Share on other sites

Ok, as a jeweler I can tell you that if this came in my store, I wouldn't secure this lug with anything other than my laser welder. Can it be soldered, probably, but no jeweler is going to want to use hard solder, so it will be done with easy solder. I can almost guarantee that the solder will flow around the crack as well as in it. This means more cleanup and being such a tight space, well, thats another reason I wouldn't use solder. Not all 18k are the same, there are different shades in color.

Lasers definitely have limitations, but in the years I have had mine, I have never had an issue with yellow gold or platinum, especially high karat gold. In the laser its like butter and produces an very secure joint. Remember that solder is a special alloy formulated for heat, while lasers use actually gold wire and basically work like a tig welder. 

Lastly, if you seek out a jeweler with a welder, make sure its a laser welder and not a puck welder. These are not as precise nor as clean in their function. Here in the states anything done on the laser starts at $30.00 and goes up from there, so it shouldn't be crazy expensive.

Good luck

  • Like 1
  • Thanks 1
Link to comment
Share on other sites

On 10/30/2018 at 1:45 PM, oldhippy said:

He doesn’t want the job.

 

Technoflux cool paste is a heat insulation paste used to protect areas not requiring heat when soldering e.g. stones, areas of metal or solder joins. The paste is applied liberally to the area, heat is then applied (during soldering),

 

You are absolutely correct on this and heat shield would be a good idea if soldering is the preferred method of repair. However, remember that when any type of heat shield is used, it essentially works as a heat sink which means the torch has to be cranked up to compensate. Being that this is an 18k lug, only an experienced jeweler should attempt this. I say experienced because here in the states, there are too many "jewelers" that are amateur at best. They think they can handle something like this and what you can be left with is a melted lug. 

  • Thanks 1
Link to comment
Share on other sites

Thanks for all the answers guys! I'm going to take the safer option of having it laser welded, a jeweller got back to me with a thorough description of how he would tackle the issue based on the pictures and a fairly reasonable quote, plus I've heard good things about him. Which is probably the biggest factor for me. Will revert back to the thread when I get it back. Fingers crossed!

Link to comment
Share on other sites



  • Recently Browsing

    • No registered users viewing this page.
  • Topics

  • Posts

    • Haha. You're just in a wicked mood today John 😅
    • Heres my watch of today, a Smith 13'" RY . My missus bought me this for this Valentines day a bargain 14.99 with a reduction, the seller has occasional 20% off offers now and then so it was about 15ish with delivery. I love Smiths and i love bulleye dials, this is my first one. The watch arrived non working as stated and i knew what was inside and what would be against me, but i enjoy a challenge, we dont expect a lot if anything from pin pallet movements. A balance pivot was broken and i didnt have another staff but i did have another RY with a battered dial so i robbed the balance and tweaked it around to make it work apart from that mostly just a good clean and relubrication. Keyless works are pretty rough by design and the crown is a bugger to get in and out with the dial on, the setting lever hits the dial before it releases it, so a little mod is needed to help that along. Major problem was the pins on the lever were quite worn which make the old tg have a snow storm fit. Its a similar read for most pin pallets, these were brass as was the escape wheel. But perseverance is me, i didn't change the pins but i did spend some time dressing and polishing the worn areas which improved the trace a lot with some straightish lines 😅 and a beat error of .5 . Not sure what the lift angle should be on these and i Wasn't in the mood to work it out and who believes timegraphers anyway, but at the default 52° it runs with 260ish full 210 after 24 hours dial down , the verticals rates were pretty much all over place. So lets just put it in it's superlight aluminium case and see what happens. Been wearing it now for 3 weeks and it's consistently losing around 1.5  minutes a week winding each morning i think pretty good for an old pin pallet watch. I just love this dial, thanks wifey heres my Valentine's gift for yer sweetie x
    • I have a PDF below that will help. The problem was the PDF wasn't designed for this purpose it was designed to tell you what size watch you  have. Then it doesn't take into account movements come conceivably in different thicknesses.   watch-ligne-size-chart.pdf