second hand face is detached


Recommended Posts

Bit of a sticky wicket that one...It appears to be a single sunk porcelain  dial from a pocket watch no? If it is, then the sub dial was soldered in place and then the dial was fired. To repair the dial can be re soldered but will the heat to do so crack or discolour the porcelain? A better option would be to use a high quality two part clear epoxy. All of this would depend on the value of the dial be it monetary or sentimental...If the dial is indeed porcelain, then the line edge would need to be addressed and sealed on the face side as well to prevent hairlines from forming. The one thing going for you is the fact it is such a clean break. Wonder how the damage happened?

Hopefully some one with dial experience will chime in...curious myself as to the best way to proceed.

Ron

 

Link to comment
Share on other sites

I would be more inclined towards the epoxy myself although the gel types of cyanoacrylate super glues are tempting to use for their convenience. Another concern I have heard of using modern glues is the aspect of off gassing contaminating the parts inside the watch...where are our dial experts when one needs them...

Ron

Link to comment
Share on other sites

Epoxy would be my choice too. I would let it cure fully, and then let it air out for at least a week or 2 to make sure all the gases have evaporated.

With soldering, I'be afraid that the expansion of the base metal would cause the enamel to crack.

  • Like 1
Link to comment
Share on other sites

Quote

 

2 hours ago, frenchie said:

Epoxy would be my choice too. I would let it cure fully, and then let it air out for at least a week or 2 to make sure all the gases have evaporated.

With soldering, I'be afraid that the expansion of the base metal would cause the enamel to crack.

Looking at the video szbalogh posted  it looks like they solder it in after enameling is done. But it is a nice clean dial, I would hate to literally toast it.

 

Link to comment
Share on other sites



  • Recently Browsing

    • No registered users viewing this page.
  • Topics

  • Posts

    • that band is old as stated, there is a kit that pops up from time to time on selling sites for the repair of these type bands, some of this type are adjustable on a few links, one adjustable type allows you to align the round opening in the expansion slit [like yours] with the rivet to separate, but if yours won't come out then the rivet head is too big and will have to be done with some rivet removal and replacement, I suppose if you could make/optain the correct rivets that one could alter the said band, the tops/caps do lift off after raising the tabs....  
    • This is a watch from a friend who sent it to a neighborhood watchmaker for a battery change. It came back with the watch stem in a ziplock bag and the dial skewed 20°. The watchmaker told him that the stem was faulty and the watch cannot be repaired. I opened up the watch and found that one dial foot was broken off and still stuck in the movement, while the other was bent until it was flat against the dial. The stem could be inserted but it couldn't be pulled out to quickset and time adjusting positions. I did a full disassemble, cleaned and oiled the movement. But when it put in the battery, the second hand runs super fast. Like it gains 30 mins every hour. Any advice on fixing this problem? TIA.
    • I determined that the balance staff is rotating, not the roller table, so my second attempt at riveting was unsuccessful. I have ordered a new balance staff and will take measurements when it arrives. The balance staff i originally ordered (and now reordered) was specified as: Replacement balance staff: (A. Schild Caliber 984 1002 1021 1124 Original Balance Staff Part 723) so it should be correct. Measurements: (see pic below for terminology) xxxyy is a place holder until the new balance staff arrives. Lower pivot: Old - .08 mm New - xxxyy Lower pivot to balance seat: Old - 1.53 mm New - xxxyy Roller shoulder: Old - .42 mm New - xxxyy Hub: Old - xxxyy New - xxxyy Balance shoulder: Old - .86 mm New - xxxyy Collet shoulder: Old - .56 mm New - xxxyy Upper pivot: Old - broken New - xxxyy
    • Hello and welcome from Leeds.  We're here to help. 
    • I was just about to adk that, probably they have unnecessary waiting lists to make their watches appear more exclusive than they actually are.
×
×
  • Create New...