Aloha and thanks for catching all these small but important details, John. I'm going to give it a shot. The good news is I have a parts movement here with a perfect complete balance. I will place them side by side for visual reference when doing what you outlined. It's been a while were I've had a hobby in which I joined a forum. I forgot just how helpful everyone can be. Mahalo. Frank. -
By Neverenoughwatches · Posted
Mike if you wanna drop me your address I'll send you a strip of this cs 100 in an envelope . I'd like your opinion of its workability The cs100 might be better carbon is 1% -
This is the link to the supplier https://springsteelstock.co.uk/cs70-c67s-carbon-steel/ -
By Neverenoughwatches · Posted
This set lever seems to working ok unhardened Nickelsilver, might it deform if i leave it that way ? I tried that method of annealing, it wasn't great but i was using unknown steel quality, old imperial feeler gauges. -
By nickelsilver · Posted
I found this from a while back CS100 seems fine, but at around 500 Vickers it's not quite as hard as "blue" steel, but still harder than annealed. I'd try to find annealed (the post above has a U.K. supplier of small quantities).
-
Recommended Posts
Join the conversation
You can post now and register later. If you have an account, sign in now to post with your account.
Note: Your post will require moderator approval before it will be visible.