PLEASE HELP - crown tube tapping


Recommended Posts

Hello i have this very rare wwii elgin canteen diver. The crown is irreplaceable so keep that in mind. The stem broke and the other half is stuck in the tube and only a tiny bit is sticking out. I have tried everything from heating it soaking it in PB blaster and I cannot break it loose I’m pretty sure it is held in by glue or some sort of Loctite. Not to mention it’s been like that for 80 years and it’s rusted. I cannot get a tight enough grip on the tiny bit that is sticking out. I think the only way out of this one is to drill it out and then re-tap it with a number eight. However I do have micro drills And a crown tap set but this needs to be done with extreme Percision and I think it is a job for a watchmakers lathe which i do not have. I am wondering if there is anyone on this forum that can do such a task. I just need help I’ll pay whatever you want. I paid $1300 for this watch and if I can’t get this crown fixed it’s pretty much only good for parts.

 

 

Sent from my iPhone using Tapatalk61938228322__BCA92755-CC25-4EE1-A19D-604AFCD7ACB2.jpg61938222321__4FC83F38-C6BE-4073-90AB-7C501ADD00A9.jpg61938223888__1583BB9D-A6A2-459F-B658-357584B8EB6C.jpg

Link to comment
Share on other sites

Hi  a bit sad, If it loctited in its going to difficult to remove in the whole. If the crown is all made of brass then using Alum (Aluminium Oxide) powder dissloved in hot water and soak the crown.  The Alum dissolves the steel but leaves the brass intact.  You are sure to get other opinions to consider and I wish you well

Link to comment
Share on other sites

Hi  a bit sad, If it loctited in its going to difficult to remove in the whole. If the crown is all made of brass then using Alum (Aluminium Oxide) powder dissloved in hot water and soak the crown.  The Alum dissolves the steel but leaves the brass intact.  You are sure to get other opinions to consider and I wish you well

I considered alum but i think the crown is steel too. The case is parkerized stainless steel, so i will assume the crown is


Sent from my iPhone using Tapatalk
Link to comment
Share on other sites

14 minutes ago, saswatch88 said:

I think the only way out of this one is to drill it out and then re-tap it with a number eight.

No. The way it's done is with a crown (hollow) mill on a lathe or boring machine. I know becuase I am being taught by a Master watchmaker that developed the below machine exactly to do that. The hollow end mill is hand made with a triangle file and then hardened. One only cuts just enough tube to grab the stem safely. I hope you can find someone that can do that for you.

esatrice_998.jpg

Link to comment
Share on other sites

No. The way it's done is with a crown (hollow) mill on a lathe or boring machine. I know becuase I am being taught by a Master watchmaker that developed the below machine exactly to do that. The hollow end mill is hand made with a triangle file and then hardened. One only cuts just enough tube to grab the stem safely. I hope you can find someone that can do that for you.
esatrice_998.jpg&key=576844ddeb0ab375d274adc4a700bf93a44c216a807bb1ac174d3a0216ce56ba

Do you think your guy can do it? I’ll pay whatever he wants. My only other option which is something I don’t want to do is basically grind the end of the stem down and re-tap the outside of the tube then use a stem adapter. Or Solder the stem directly to the tube. Both these options would be what I consider rigged and I am a stickler for details especially when it comes to these extremely rare watches


Sent from my iPhone using Tapatalk
Link to comment
Share on other sites

This may be a really stupid suggestion, but it can't hurt to throw it out there in case it sparks a better idea.

On a MUCH larger scale I've seen people use an arc welder, hook the ground to the part with the broken off "bolt", file the exposed surface of the broken threaded piece so it's flat, then hook the "positive" wire to a junk bolt that has a similarly prepped face, then touch the bolt to the broken off stud and the bolt gets welded to the broken off part. Then use a wrench to turn the broken off part out.

That said, if the stem broke in the first place whatever thread locker is holding it in the crown is probably is strong enough that what you tack weld to it in this manner would also just snap off.

What is the diameter of the original stem?

Link to comment
Share on other sites

12 minutes ago, saswatch88 said:

Do you think your guy can do it? I’ll pay whatever he wants.

Answered in PM and for the record not for money.

My other observation is that on lathe, even a "model engineer" one with a collet chuck it is trivial to cut 1 or 2 mm off the tube.

Edited by jdm
Link to comment
Share on other sites

This may be a really stupid suggestion, but it can't hurt to throw it out there in case it sparks a better idea.
On a MUCH larger scale I've seen people use an arc welder, hook the ground to the part with the broken off "bolt", file the exposed surface of the broken threaded piece so it's flat, then hook the "positive" wire to a junk bolt that has a similarly prepped face, then touch the bolt to the broken off stud and the bolt gets welded to the broken off part. Then use a wrench to turn the broken off part out.
That said, if the stem broke in the first place whatever thread locker is holding it in the crown is probably is strong enough that what you tack weld to it in this manner would also just snap off.
What is the diameter of the original stem?

Yes I have heard of that before but the problem is I don’t think there is nearly enough sticking out to weld. I don’t know the size I just know it is a tap 8 stem


Sent from my iPhone using Tapatalk
Link to comment
Share on other sites

I don’t think you want to attempt to cut into the existing stem as it will likely be harder than the crown pipe. 

If it’s any consolation, I recently repaired an original irreplaceable crown on a £7k JLC Mk11 and it worked out fine. 
 

There are many ways to skin a cat, but here is what I would do:

Firstly, I’d find out if the crown pipe is stainless, or at least significantly less likely to corrode than a carbon-steel stem. Usually this will be the case. Which opens up the opportunity to dissolve the stem in acid.

To dissolve with acid, you can suspend the crown such that only the end of the pipe is sitting in the acid. You can use an oiler to spread the rest of the pipe with silicone grease to acid-proof it. I’ve attached a photo of a crown from a 1980’s issued Precista military diving watch having this done just now. The corroded stem gathers at the bottom of the container.

 

FD98AE49-DBAF-4CCB-B330-14B25A8C7224.jpeg

  • Like 1
Link to comment
Share on other sites

53 minutes ago, watchweasol said:

using Alum (Aluminium Oxide) powder

Actually aluminium oxide is an abrasive grit, not soluble in water, and pretty inert.

Alum is potassium aluminium sulphate, water soluble and will dissolve steel but not brass, and not stainless steel.

I would be surprised if the crown were a plain carbon steel as this would make it rather prone to rusting as it's exposed to the outside world. If it's stainless or brass though then alum is your answer.

  • Thanks 1
Link to comment
Share on other sites

Actually aluminium oxide is an abrasive grit, not soluble in water, and pretty inert.
Alum is potassium aluminium sulphate, water soluble and will dissolve steel but not brass, and not stainless steel.
I would be surprised if the crown were a plain carbon steel as this would make it rather prone to rusting as it's exposed to the outside world. If it's stainless or brass though then alum is your answer.

Ok It is 100% stainless steel. What is the correct name for the solution I need to look for. I will just go to my local Home Depot


Sent from my iPhone using Tapatalk
Link to comment
Share on other sites

I don’t think you want to attempt to cut into the existing stem as it will likely be harder than the crown pipe. 
If it’s any consolation, I recently repaired an original irreplaceable crown on a £7k JLC Mk11 and it worked out fine. 
 
There are many ways to skin a cat, but here is what I would do:
Firstly, I’d find out if the crown pipe is stainless, or at least significantly less likely to corrode than a carbon-steel stem. Usually this will be the case. Which opens up the opportunity to dissolve the stem in acid.
To dissolve with acid, you can suspend the crown such that only the end of the pipe is sitting in the acid. You can use an oiler to spread the rest of the pipe with silicone grease to acid-proof it. I’ve attached a photo of a crown from a 1980’s issued Precista military diving watch having this done just now. The corroded stem gathers at the bottom of the container.
 
FD98AE49-DBAF-4CCB-B330-14B25A8C7224.thumb.jpeg.dd54fbf0876e6225673a25377432831d.jpeg

What solution did you use


Sent from my iPhone using Tapatalk
Link to comment
Share on other sites

10 minutes ago, saswatch88 said:

Ok It is 100% stainless steel. What is the correct name for the solution I need to look for. I will just go to my local Home Depot

As @watchweasol alludes to it's an astringent used in old fashioned wet shaving.

I use this as I have it around anyway (being convinced that the peak of shaving technology was reached in the late 1800's to early 1900's and everything else since has just been marketing hype to part a man and his money) and it works fine.

Interestingly enough as well as a shaving product, and for dissolving steel, it also makes an excellent un-perfumed deodorant, and is used as a food preservative, so you might be able to pick it up in the food aisle at your local supermarket in powder form.

Link to comment
Share on other sites

17 minutes ago, saswatch88 said:


What solution did you use


Sent from my iPhone using Tapatalk

Phosphoric acid. I wouldn’t bother with alum as you’ll be waiting until next year for it to finish off!

Link to comment
Share on other sites

3 minutes ago, rodabod said:

I wouldn’t bother with alum as you’ll be waiting until next year for it to finish off!

Usually no more than about 3 days. Quicker if you keep it warm.

Link to comment
Share on other sites

I do use alum, but I find it can be very slow when dissolving stems which are trapped as there is so little material exposed. 

It seems not one grocery store has alum in stock but i can get phosphoric acid. The tube is stainless steel but it was treated and it is not magnetic. The stem however is since its carboned steel. Will the acid ruin the tube too?


Sent from my iPhone using Tapatalk
Link to comment
Share on other sites

I mix up my alum, put it in a urine container/jar, then I drop it into a thermos full of boiling water for 3 days. Longer if needed.
I'd persevere with the alum. It will eventually get the job done.
Seiko use stainless steel stems in some models. I have been unable to dissolve a diving watch stem recently.

Link to comment
Share on other sites

2 hours ago, AlexeiJ1 said:

I mix up my alum, put it in a urine container/jar, then I drop it into a thermos full of boiling water for 3 days.

Starting with the 1.3L model, ultrasonic cleaners come with heating. They are not expensive and ideal for maintaining a controlled temperature over time. Of course you would have to place the alum setup in bain-marie. 

  • Like 1
Link to comment
Share on other sites

On 8/17/2020 at 11:33 PM, saswatch88 said:


It seems not one grocery store has alum in stock but i can get phosphoric acid. The tube is stainless steel but it was treated and it is not magnetic. The stem however is since its carboned steel. Will the acid ruin the tube too?


Sent from my iPhone using Tapatalk

Whereabouts are you? If in UK I can send a small amount of Alum. 

Cheers,

Phil

Link to comment
Share on other sites



  • Recently Browsing

    • No registered users viewing this page.
  • Topics

  • Posts

    • This is a very sad day for the industry.. For most of us being amateurs the cost of replacing parts for ETA,s etc will be beyond affordability for the customers.   see full statement below   We have now received the decision from Judge Michael Green on whether or not the High Court has jurisdiction to hear our claim against Swatch, and sadly it is not the decision we had hoped for.   As we have pointed out in previous news items (see below),the rules that Judge Green had to apply strictly prevented him from examining in any way how the Swiss Court arrived at its verdict, even if it is blatantly obvious that the verdict is wrong.   As Swatch’s lawyer was summing up in the last few minutes oft he hearing, the Judge twice pinned him asking if it was alright if, as a result of the Swiss verdict, consumers had to pay 50% more for their watch repairs. After some stumbling, their lawyer’s reply was “Yes”, so  I am quite sure that Judge Green left his court fully aware that the Swiss verdict does not reflect the norms of British Competition Law. However, the rules simply do not allow him to take that simple fact into account.   Judge Green noted that our two arguments relating firstly to British Competition Law now being different from that of the EU, and secondly to the contention that the legality of the Authorised Service Networks has not been tested, had both been mentioned in the Swiss verdict. Because they had been mentioned, he felt that to allow us to argue them again would constitute re examining the Swiss case, and could not be allowed.   As to our claim that we were denied our right to be heard because our evidence was not considered, our lawyers had argued that the evidence we provided could not have been looked at because had the Swiss Court done so, it could not have reached the conclusion that it did. In his verdict, Judge Green highlighted general statements in the Swiss verdict that evidence had been looked at, and acknowledged the arguments we made to him, but again he considered that this was re-examining the Swiss verdict, and could not be permitted.   Our case has attracted considerable interest within the Legal community, and within minutes of the decision being made public we were approached for comment by one of the largest subscription news services, Global Competition Review. They asked us two very pertinent questions, and I reproduce them for you below along with our responses, as they neatly summarise the consequences arising from our case.   What are the key takeaways?   Enormous damage has been done to the fundamentals of UK and European Competition Law by the Swiss courts. It has always been the case that the effect on consumers and competition has to be considered in any decision making, but we now have a ruling that states even monopolists can remove wholesale markets from the supply chain without any consumer benefit based justification. Those entities looking to subvert Competition Law and exploit consumers for their own benefit will be looking at this very carefully.   Has the court made the wrong decision? If so, will you appeal?   The issue lies not with the High Court, but rather with cross border jurisdiction treaties that have no requirement in them for foreign jurisdictions applying UK law to take account of the Ratio Legis [a legal term for the fundamental reasoning why the law was written] of that law, and have no remedy within them for UK Courts to overcome decisions that clearly do not.    After eight years of work, and a very considerable sum in legal costs, I can not begin to tell you how disappointed I am at this outcome. For the time being, there is no further route through the British Courts that Cousins can follow. However, I promised that we would fight to the end, and that promise stands.   The UK is no longer part of the Lugano Convention, whose rules Judge Green has applied, and as yet nothing permanent has replaced it. The political tide turned against repair prevention by restricting supply of spare parts some time ago, and our efforts on behalf of the Watch Repair industry have resulted in high level contacts within several Government Departments. You can be sure that we will keep working to overcome this unjust situation that we now all find ourselves in.    I will keep you advised.   Kind regards   Anthony
    • Dell fancy a challenge🤣   https://www.ebay.co.uk/itm/285785684626?itmmeta=01HT29WVJY21Q94C73GYHGBTFX&hash=item428a277a92:g:15YAAOSwNRVmBAUz&itmprp=enc%3AAQAJAAAA0DIe4QLQBW66rSyIMiyBuk8GY%2B86pQ%2BQnxGbcNq7egAGe5DIs9YMmiWJIbZtMSxwNJIiJxuojbq523IeUSBQ6pJEIQ0tfz2ChrBR03BksmKINyklg1IK4GAfAcYY9Hta9wVeSZSZN7ZCNAfZTgKs9c4%2BUIUZ3Qjc3QjUXDn2uPRo1FiYOEewMG5A26EXb%2BclBgrqtbOmM6P3bea%2F8ZImOAXNI1HtbmtMk84pIGoM6ISwaM1PKFuADtTFMccS5e3ZjndCbXYXHrW3CecsV0edw3M%3D|tkp%3ABk9SR8q588nQYw Darwin’s theory of evolution has not been proven to be absolutely.  😀 
    • A already know the size movement I have the problem is the dial a had purchased has a dimension 20.6mm wide a want to find a watch case that going to fit the dial perfectly 
    • Hi.  I would like to take issue here regarding battery driven , watches, clocks,etc. I will and do repair these clocks in fact I have sever al in my collection as well as the regular mechanical ones. I have one on my mantle piece over 60 years old tha belonged to my wife’s Aunt,  long gone Iam afraid and it has been cleaned etc and never missed a beat and is accurate. Every one has their preduices as regards Electrical /electronic Horology but I regard it as part of the progress time line of the art of Horology and to be treated as such. Like Darwin’s theory of evolution it evolved.  Two cavemen knocking rocks together and a shard broke off , looking at it he worked out if it was stuck on the end of a stick he would have a spear. Likewise his pal seeing what he was up to picked up a piece  and did the same, now that’s evolution. Some clockmaker decided to build a clock that ran with a battery and no spring to wind up and break, progress and both the mechanical and battery driven clocks evolved, the battery ones got better to the point that if it broke you changed the complete unit. Likewise watches did the same but both can be repaired by people who approach Horology with an open mind without preduice.  We all have our likes and dislikes bu I for one would never dismiss any technology because I don’t like it.   The mobile phone is a good example of modern technology at work as is the automotive industry. There buttons and switches in my car I don’t use because to me they are not nesessary but I still drive the car.
    • I haven't gone through all the reading of what it might be or not. The first thing I would do if nothing obvious stands out is replace the mainspring, you have to start at the source of the power. Nine times out of ten that is the problem.  
×
×