Hi there can anyone help me with this movement that I have purchased to repair.The top pivot on the balance staff is broken and I am trying to find out who this movement is made by so I can attempt to get a replacement staff.On the movement it is stamped V.W.C. in an oblong box but I am unable to find out anything else.Photo enclosed.Any help would be gratefully received.Keep safe and stay home.Regards, Sethnettles.Screenshot_20200408-170127.thumb.png.875bc8f42449ece1828134bf55436739.png

Link to comment
Share on other sites
Seth Watch Enthusiast

Seth

Posted
  • Author
Posted

Hi all,many thanks for all your help and replies I can now look for a replacement balance staff after I have done some measurements.Regards and keep safe, Seth.

Link to comment
Share on other sites
 Share
Go to topic listing


  • Recently Browsing

    • No registered users viewing this page.

  • Topics

  • Posts

    • mikepilk
      Setting lever spring

      By mikepilk · Posted

      I would harden and temper (to a light blue). It's so easy to do and only takes a couple of minutes. A search on ebay UK for "spring steel strip cs" finds plenty available in small quantites and thicknesses from 0.1mm up.  But the question is ( @nickelsilver) which "CS" number is best for watch parts ?  Also, from one of the ads : "CARBON SPRING STEEL. SIZE IS METRIC 15.00mm X 0.10mm X 304 MM  CS100 FINISH BRIGHT . HARDENED AND TEMPERD TO 480-530VPN" I've no idea about 480-530VPN. Does that mean it needs annealing before working?      
    • Waggy
      Movement holder made with 3D printer

      By Waggy · Posted

      Here is the insert ring for rectangular or elliptical movements: Note that the length is the side with the stem cut out on the spreadsheet (in the picture below this is 15.15: Here is the fake pdf file, again you need to convert to .zip after download to access the FreeCAD and 3mf files. Rectangular insert disc.pdf    
    • JohnR725
      Omega cal. 565 - low amplitude

      By JohnR725 · Posted

      as you took the mainspring out what did it look like? It's amazing how much amplitude you can get if the mainspring actually has the proper shape. last week I was doing a 12 size Hamilton and was very much surprised with the beautiful back curvature the mainspring had. Then the watch had a really nice amplitude the group would be so proud it was 350 until I dropped the lift angle down to 38 that drop the amplitude quite a bit below 300. then with the beautiful back curve it still had really nice amplitude the next day. I really wish all my mainspring's look like this as the watch had beautiful amplitude the next day. So many of the aftermarket pocketwatch Springs I see now do not have anything resembling a back curve may be a slight curve and that's about all. They still work but they just don't work as nice as a properly made spring. then Omega as all sorts of nifty technical documentation unfortunately every single corner is watermarked with where it came from who downloaded it etc. very paranoid company. On the other hand I will snip out images like from the document on recycling a mainspring barrel. for instance here's the section on what your mainspring should look like. water damaged a lot of times means rust was there rust on this watch?
    • RichardHarris123
      Without Our Forum

      By RichardHarris123 · Posted

      I wondered that?
    • Neverenoughwatches
      Without Our Forum

      By Neverenoughwatches · Posted

      I dont understand why a patreon membership would have limited places ??
×
×
  • Create New...