Can acrylic cracks be fixed ?


Chopin

Recommended Posts

Hello guys, I come with a question for those of you that probably have experimented around.

I have a watch with a crystal that has a few small hairline cracks (all the way down, so to speak) and I was just wondering if it wouldn't be possible to have them fixed/covered/filled by simply applying some type of adhesive that enters the cracks. I'm asking because I recently saw a video of someone fixing a cracked windshied by inserting some transparent adhesive into the cracks and they eventually disappeared as the adhesive dried.

The watch has a bit of an unusual crystal. I ordered an ATCH crystal but apparently it wasn't perfect. Apparently the vertical outer wall isn't as long as the old one (basically 2/3 through it starts to curve; measured bottom to top). (photo of the old one below, in case someone could help me name this type of crystal)

IMG-8559.jpg

Link to comment
Share on other sites

I suspect it may be possible, but equally it may be more problematic than it first appears.
 

  1. One major issue is that any dirt in the crack will end up set in the repair compound, so unless you can ensure absolute cleanliness then the crack may still be noticeable following the repair.
  2. You may need to pull a vacuum to get the repair material to enter the cracks.
  3. You will still need to polish the piece after the repair to ensure an optically acceptable finish.
  4. The repair material will need to set up (cure) with roughly the same refractive index as the original material.

    For the record, most of these crystals are probably a form of poly-carbonate, but this may not always be the case, and you would need to confirm what the crystal is made from to ensure the repair compound is compatible.
Link to comment
Share on other sites

Can be done . Have repaired some with acrylic powder and the solution for nails. Same that is used for prosthetics . But it doesn't work if it's in the middle of the crystal . It can be polished up to near perfect finish as it's the same material. You need to remove the old crack and get into the material that is good . Then fill it with acrylic. 

What size crystal do you need . And for what watch? 

I have a Certina DS 2 i crystals with similar cracks  can have a go at . And i can do a before and after. Have some powder left i think. Tomorrow evening. 

Edited by rogart63
Link to comment
Share on other sites

Thanks guys, so that would be a no on my part, then.

It's not the size that is the problem but the height of the vertical edge/wall of the crystal. The ATHC starts to curb halway while the one that I need needs to be straight/vertical almost to the top of the overall height of the crystal (as the photo shows). I just don't know what type of crystal it is since it's clearly not an ATHC.

Link to comment
Share on other sites



  • Recently Browsing

    • No registered users viewing this page.
  • Topics

  • Posts

    • people be honest.... Swatch is evil for the watchmakers and repairers, BUT not everything in watches from Switzerland is from the Swatch-Group. As far as i know, Selitta got sacked by Swatch as a Movement-Assembler for them and they started to produce Movements in their own Name with slight Modifications. As far as i know, they sell Parts to the Market for their Movements. In most cases, if a ETA-Movement fails, it is a valid Option to replace it with a Selitta Movement, which i consider the Solution for this Mess with the Swatch-Group...... I have no Connection to anybody at Selitta, but being a Swiss-Guy, i still like to have Swiss-Made Watches, but not from the Swatch-Group.   ok ? regards, Ernst
    • Just one more greedy act by Swatch. They started a number of years ago here in the US..cutting off supplies to watchmakers that could build complications that many Swatch houses couldn't even touch. Old school masters who had gone through some of the most prestigious houses in the world. Otto Frei has some statements on their page about it. I tell all my customers to avoid new Swiss watches like the plague,..unless they just want an older one in their collection that still has some parts out on the market, or they have really deep pockets and don't mind waiting months and paying through the nose to get it back. Plenty of others to choose from..IE Seiko,..or other non-swiss brands Even a number of Chinese brands are catching up with the Swiss,..and I think that in time, their actions will be their downfall
    • Yes. If that's not what you are experiencing...start looking for something rubbing. A 1st guess is that one of the hands is rubbing against the hole in the center of the dial. Especially if you now have lower amplitude in face up/ face down positions.
    • Once a movement has the dial and hands put back and it is recased, would you expect the assembled watch to have the same amplitude as when the movement is in a movement holder and is without hands and dial? Thanks
    • C07641+ not sure what the "+" is for after the last digit.
×
×
  • Create New...