Yes it does, but not enough to endanger the fitting of the pivot into the hole. Burnishing removes the faint marks left in the steel after turning/alteration due to wear or cutting a new pivot. It creates an extremely fine finish, like a mirror finish. It also helps in the rotation of the pivot, preventing it from binding in the hole. If you gauged before and after I don’t think it would change, providing the work has been carried out correctly.

  • Like 2
Link to comment
Share on other sites
nickelsilver Distinguished Member

nickelsilver

Posted
Posted

It does remove (and compress) material, but it could be just a micron or two to several hundredths or more. Burnishers as used on pivots always have a straight grain texture, this is in effect a micro file. When burnishing on a Jacot tool you are removing a small amount of material as well as work hardening it. It does increase the wear resistance of a pivot. When I make a balance staff I generally leave the pivots 0.01-0.02mm oversize and bring them down to final size in the Jacot tool.

Link to comment
Share on other sites
 Share
Go to topic listing


  • Recently Browsing

    • No registered users viewing this page.

  • Topics

  • Posts

    • Neverenoughwatches
      Setting lever spring

      By Neverenoughwatches · Posted

      As an experiment i was thinking of not hardening it to see how it fairs. Now that i have a complete template i could knock up another in half the time if this loses its elasticity. I might play about with a few pieces today to test their bending and spring properties. This was cs 100 the supplier quoted in annealed state, it was nice to work with files so I'm taking it thats its state. What you are looking seems like it would need annealing to work it. This is why i went for this stuff that cuts out that process, it was so easy to work.
    • dnhb
      Is this a 'hack' ?

      By dnhb · Posted

      Showing state of hairspring on receipt, backplate & 'dished' wheel. 
    • mikepilk
      Setting lever spring

      By mikepilk · Posted

      I would harden and temper (to a light blue). It's so easy to do and only takes a couple of minutes. A search on ebay UK for "spring steel strip cs" finds plenty available in small quantites and thicknesses from 0.1mm up.  But the question is ( @nickelsilver) which "CS" number is best for watch parts ?  Also, from one of the ads : "CARBON SPRING STEEL. SIZE IS METRIC 15.00mm X 0.10mm X 304 MM  CS100 FINISH BRIGHT . HARDENED AND TEMPERD TO 480-530VPN" I've no idea about 480-530VPN. Does that mean it needs annealing before working?       Have you seen this video, he shows how to determine where the indents go ?  
    • Waggy
      Movement holder made with 3D printer

      By Waggy · Posted

      Here is the insert ring for rectangular or elliptical movements: Note that the length is the side with the stem cut out on the spreadsheet (in the picture below this is 15.15: Here is the fake pdf file, again you need to convert to .zip after download to access the FreeCAD and 3mf files. Rectangular insert disc.pdf    
    • JohnR725
      Omega cal. 565 - low amplitude

      By JohnR725 · Posted

      as you took the mainspring out what did it look like? It's amazing how much amplitude you can get if the mainspring actually has the proper shape. last week I was doing a 12 size Hamilton and was very much surprised with the beautiful back curvature the mainspring had. Then the watch had a really nice amplitude the group would be so proud it was 350 until I dropped the lift angle down to 38 that drop the amplitude quite a bit below 300. then with the beautiful back curve it still had really nice amplitude the next day. I really wish all my mainspring's look like this as the watch had beautiful amplitude the next day. So many of the aftermarket pocketwatch Springs I see now do not have anything resembling a back curve may be a slight curve and that's about all. They still work but they just don't work as nice as a properly made spring. then Omega as all sorts of nifty technical documentation unfortunately every single corner is watermarked with where it came from who downloaded it etc. very paranoid company. On the other hand I will snip out images like from the document on recycling a mainspring barrel. for instance here's the section on what your mainspring should look like. water damaged a lot of times means rust was there rust on this watch?
×
×