Question About Old Watchmakers Desk

jdrichard

By jdrichard
in Tools & Equipment

 Share

Recommended Posts

jdrichard Distinguished Member

jdrichard

Posted
Posted

I was asked by the curator of the Canadian Clockmakers Museum what the small pocket on the lower right side of the desk is used for. It is next the the small poster and bottom right part of the desk, just below the desk top and about 3 inches wide by 6 inches tall.7d72dfd66397c90260c86bbe01df29e8.jpg

 

 

Sent from my iPhone using Tapatalk Pro

Link to comment
Share on other sites
nickelsilver Distinguished Member

nickelsilver

Posted
Posted

I will look this up. What specifically did they use it for?


Sent from my iPhone using Tapatalk Pro
They would load a bristle brush with it and brush down the parts. Sounds crazy I know, but that was part of good cleaning procedure 120 something years ago.

Goodrich's book The Watchmaker's Lathe its Use and Abuse has and illustration describing the chalk hole.
  • Like 1
Link to comment
Share on other sites
jdrichard Distinguished Member

jdrichard

Posted
  • Author
Posted
They would load a bristle brush with it and brush down the parts. Sounds crazy I know, but that was part of good cleaning procedure 120 something years ago.

Goodrich's book The Watchmaker's Lathe its Use and Abuse has and illustration describing the chalk hole.

Thanks. I have that book and will look this up

Sent from my GT-N5110 using Tapatalk

Link to comment
Share on other sites
vinn3 Distinguished Member

vinn3

Posted
Posted
13 hours ago, jdrichard said:


It’s just a square opening in the desk???


Sent from my iPhone using Tapatalk Pro

    i was looking at something else on the bench top !!!      put a circle around something on the bench top,   i'll try again - vin

Link to comment
Share on other sites
nickelsilver Distinguished Member

nickelsilver

Posted
Posted

For those who are curious, French chalk is basically magnesium silicate, talc. It's the lowest number on the Mohs scale for minerals.

 

Another mineral traditionally used in watchmaking is Spanish powder, or blanc de meudon or blanc d'espagne. This is calcium carbonate (primarily), slightly more aggressive as an abrasive. On a watch with gilded plates and bridges, when they are tarnished/stained and unaffected by normal cleaning methods, this stuff can be rubbed on wet with fingers or brush. It does an amazing job of brightening the parts, without leaving a scratch. Calcium carbonate is the main component of blackboard chalk, so if your local drugstore doesn't have it* crush some up and give it a try.

 

 

*we're really spoiled in my area with a drugstore thathas all kinds of cool stuff. Just got silver nitrate there for a new batch of dial silvering powder.

 

 

Link to comment
Share on other sites
jdrichard Distinguished Member

jdrichard

Posted
  • Author
Posted
For those who are curious, French chalk is basically magnesium silicate, talc. It's the lowest number on the Mohs scale for minerals.
 
Another mineral traditionally used in watchmaking is Spanish powder, or blanc de meudon or blanc d'espagne. This is calcium carbonate (primarily), slightly more aggressive as an abrasive. On a watch with gilded plates and bridges, when they are tarnished/stained and unaffected by normal cleaning methods, this stuff can be rubbed on wet with fingers or brush. It does an amazing job of brightening the parts, without leaving a scratch. Calcium carbonate is the main component of blackboard chalk, so if your local drugstore doesn't have it* crush some up and give it a try.
 
 
*we're really spoiled in my area with a drugstore thathas all kinds of cool stuff. Just got silver nitrate there for a new batch of dial silvering powder.
 
 

Again, thanks very much. I will pass this info along to the curator of the clock museum.


Sent from my iPhone using Tapatalk Pro
Link to comment
Share on other sites

Join the conversation

You can post now and register later. If you have an account, sign in now to post with your account.
Note: Your post will require moderator approval before it will be visible.

Guest
Reply to this topic...

×   Pasted as rich text.   Restore formatting

  Only 75 emoji are allowed.

×   Your link has been automatically embedded.   Display as a link instead

×   Your previous content has been restored.   Clear editor

×   You cannot paste images directly. Upload or insert images from URL.

×
 Share
Go to topic listing


  • Recently Browsing

    • No registered users viewing this page.

  • Topics

  • Posts

    • JohnR725
      Omega cal. 565 - low amplitude

      By JohnR725 · Posted

      as you took the mainspring out what did it look like? It's amazing how much amplitude you can get if the mainspring actually has the proper shape. last week I was doing a 12 size Hamilton and was very much surprised with the beautiful back curvature the mainspring had. Then the watch had a really nice amplitude the group would be so proud it was 350 until I dropped the lift angle down to 38 that drop the amplitude quite a bit below 300. then with the beautiful back curve it still had really nice amplitude the next day. I really wish all my mainspring's look like this as the watch had beautiful amplitude the next day. So many of the aftermarket pocketwatch Springs I see now do not have anything resembling a back curve may be a slight curve and that's about all. They still work but they just don't work as nice as a properly made spring. then Omega as all sorts of nifty technical documentation unfortunately every single corner is watermarked with where it came from who downloaded it etc. very paranoid company. On the other hand I will snip out images like from the document on recycling a mainspring barrel. for instance here's the section on what your mainspring should look like. water damaged a lot of times means rust was there rust on this watch?
    • RichardHarris123
      Without Our Forum

      By RichardHarris123 · Posted

      I wondered that?
    • Neverenoughwatches
      Without Our Forum

      By Neverenoughwatches · Posted

      I dont understand why a patreon membership would have limited places ??
    • clockboy
      Hi all

      By clockboy · Posted

      Welcome to the forum, enjoy. It’s highly unlikely you will be able to purchase a new bezel look on eBay for a pulsar watch for repair to find a bezel.
    • JohnR725
      Balance spring fell out of regulator pin.

      By JohnR725 · Posted

      just one little minor reminder here this isn't your normal balance wheel.  pages 17 and 18 are what you really want to be looking at. normally studs don't turn but this watch has the etachron system designed for lots of adjustment. Personally I would try to rotate the stud back to where it's supposed to be. If you're lucky you didn't actually bend it at the stud it just looks really bad as the stud has been rotated grossly out of position.. I think things will look a lot better if you put the hairspring back where it's supposed to be by rotating the stud. it's hard to tell if you actually did bend it at the stud or not we won't know until you rotate the stud back more or less where it's supposed to be. Then you want to pay attention to the manual of how to put the hairspring back in the regulator pins because yes they rotate also and they rotated specific directions otherwise bad things will happen to your hairspring. so initially you can open up the regulator as wide as it can go and don't worry about closing it until thing everything is right then you can close them a little bit
×
×