I've just bought a small amount of the Horotec Episurf-Neo, which is advertised as a 'next gen' epilame treatment.

Directions for use say 30 second dip, 60 second dry at air temperature. So no heat required.

I too am looking for a cheap DIY alternative to the special dip bottle. I've been experimenting with the little filter baskets from the water inlets on washing machines! Haven't found the perfect solution yet, but I'm working on it!

 

 

IMG_1764.jpg

  • Like 1
Link to comment
Share on other sites

  • 1 year later...

I was thinking about using Fixodrop but  have a hard time figuring out what parts to use it on. The fewer the better considering the abhorrent price for it. What I got so far.

* Pallet jewels

* Escape wheel

* Reversing wheel on automatic

* Balance End stones

 

What is your opinion on this ? Should the end stones be treated, and if so, does that include the chaton ? 

Link to comment
Share on other sites

https://www.cousinsuk.com/category/moebius-fixodrop-fk    This link will give you ther page on Cousins site regarding fixodrop/Epilame  not only is it expensive, there are also hazzards in using it as explained in the following link  http://watchmakingblog.com/2011/07/29/one-hazard-of-epilame/.  I would suggest reading both and makining an informed descision         cheers

  • Like 1
  • Thanks 3
Link to comment
Share on other sites

17 minutes ago, oldhippy said:

I myself never used such stuff, not sure if it was around in my days, besides I had a very steady hand.  

Yes it was, 1957 Omega literature explains it, in the 60s Greiner made a machine to apply it from bags of stearic acide, after ultrasonic cleaning.

I've neither used it so far, I think that today's quality of lubricatints helps doing without it, at the same time I don't have enough experience to recommend one way or the other.

Link to comment
Share on other sites

  • 3 weeks later...
15 minutes ago, praezis said:

Don't forget to run the movement dry for some minutes, before oiling.

Frank 

You should never run a movement dry. It needs lube no matter for how long. More then likely you will need to add oil as you re assemble the movement as the more you add parts the more difficult to oil certain parts become. 

Link to comment
Share on other sites

In csse of runing movements, I take dial and disk plates off, wind full and drop the whole movement in avgas( absolutely friendly to shelac) , if it ran whilst submerged, I lets it run overnight to clean itself, then disassemble it for clean& service. 

 My late repairman frowned on this practice of mine but never explained the reason. 

This is a chance to put my question to vote, your thoughts please.

Link to comment
Share on other sites

In csse of runing movements, I take dial and disk plates off, wind full and drop the whole movement in avgas( absolutely friendly to shelac) , if it ran whilst submerged, I lets it run overnight to clean itself, then disassemble it for clean& service. 
 My late repairman frowned on this practice of mine but never explained the reason. 
This is a chance to put my question to vote, your thoughts please.
By avgas you mean kerosene I guess? Why not, I don't think it will hurt anything, but getting all of that cleaned off would eat a lot of solvent or cleaning solution.
  • Thanks 1
Link to comment
Share on other sites

1 hour ago, Nucejoe said:

In csse of runing movements, I take dial and disk plates off, wind full and drop the whole movement in avgas( absolutely friendly to shelac) , if it ran whilst submerged, I lets it run overnight to clean itself, then disassemble it for clean& service. 

 My late repairman frowned on this practice of mine but never explained the reason. 

This is a chance to put my question to vote, your thoughts please.

 

giphy.gif

  • Thanks 1
  • Haha 2
Link to comment
Share on other sites

33 minutes ago, nickelsilver said:

By avgas you mean kerosene I guess? Why not, I don't think it will hurt anything, but getting all of that cleaned off would eat a lot of solvent or cleaning solution.

Aviation gas = avgas ,  I am not sure if this grade of avgas runs piston airplane or turbine engines( diferent I hear), but has no effect on shelac and no visible effect on base metals either. 

Some calibers wont run while submerged. 

Thanks for your response.

Link to comment
Share on other sites

15 minutes ago, oldhippy said:

It’s one way of causing extra wear on a movement, pivots could shear off, all sorts of damage could happen. 

Oh I mean submerged and running with oscilator, so runs at low speed, if thats your concern, amplitude also drops.

 

Link to comment
Share on other sites

I’ve done something similar to what Nucejoe describes when doing a “pre clean” on an utterly filthy movement with L&R cleaning solution. Personally, I don’t see any great risk of harm. The aviation fuel probably provides a reasonable amount of lubrication for the short amount of time that it is running. 

Link to comment
Share on other sites

Avgas has lead in it. Is it enough? No idea. It’s 100 (min) octane gasoline.  Turbines (jets) run on Jet-A which is essentially kerosene. 
 

I had also considered such action at times (with Ronsinol) but never did. Cleaning is always better when you have access to both sides of plates. 

Edited by Tudor
Link to comment
Share on other sites

On 8/29/2020 at 3:44 PM, nickelsilver said:

Run the movement with the pallet jewels dry for some minutes, this allows the escape teeth to scrape off the epilame from them and that non-epilamed "track" holds the oil.

Thanks, nickelsilver!

I was referring to the epilame treated parts only, acording the topic.

Frank

Link to comment
Share on other sites

One of the problems with watch repair is the age of the technical information. A problem with the age of the material is it's possible that things have changed like even fixodrop? Like for instance at the link below there is variations lots of them? Plus they've changed the solvent to something more environmentally supposedly friendly. Changing the solvent has had other interesting changes.

For instance 7061 This one's interesting wash resistant if you download the technical sheet it tells how to apply it. Then since I really enjoyed the answer "NO" up above I'm going to quote something "Fixodrop-treated anchor pallets should be lubricated only after running dry for 1 to 2 minutes" Unlike the answer "NO" up above it's okay because it's only the pallet stones. You need to remove the surface treatment so the oil will stick otherwise you're going to have issues.

Then they explain the drying procedure. This is interesting because the previous solvent they were using would evaporate so fast that if you weren't very very careful the cooling effect would cause moisture to condense out of the air eaving a microscopic coloring of moisture on your nice clean steel parts which leads to rust. This is why shops using this a lot of times I have a hot hairdryer radius and is a part came out that immediately put hot air on to hopefully avoid this. Now it's supposed to be better and not have that happen.

On 8/9/2020 at 10:12 AM, Flubber said:

Should the end stones be treated, and if so, does that include the chaton

 

Only the end stone should be treated not the setting.

 

 

 

http://www.moebius-lubricants.ch/en/products/epilames

  • Thanks 1
Link to comment
Share on other sites

Join the conversation

You can post now and register later. If you have an account, sign in now to post with your account.
Note: Your post will require moderator approval before it will be visible.

Guest
Reply to this topic...

×   Pasted as rich text.   Restore formatting

  Only 75 emoji are allowed.

×   Your link has been automatically embedded.   Display as a link instead

×   Your previous content has been restored.   Clear editor

×   You cannot paste images directly. Upload or insert images from URL.




  • Similar Content

  • Recently Browsing

    • No registered users viewing this page.
  • Topics

  • Posts

    • Thank you so much, Hector and CJ. I appreciate the tech sheet and the video. Gasp, I think I will make the attempt. What's the worst that can happen? I think there may be a new balance complete in my future, though.  I'll update the post and let you know the result. R, Frank  
    • So here is the new base (v 2.1), I made it so that the base will fit over and swallow the stump of the hand pusher tool (or at least my clone of the tool), I also reduced the OD of the bottom skirt a little as it looked/felt a little large, here are a few pictures and the fake .pdf file which you need to convert to .zip once downloaded.   The cut-out seen on the below image on the bottom of the base should swallow the OD (40 mm, +0.1 mm tolerance) of the stump and the height of the stump 9.5mm (measured to 9.1mm, but rounded to 9.5mm) - let me know if this works for your tool.   Note, I think you may need to print supports for the new internal shelf created? Here is the fake .pdf for just the FreeCAD base file and 3mf files Modular Movement Holder.pdf Here is the fake pdf for complete set of the new base and ring FreeCAD/3mf files: Modular Movement Holder base and ring v 2.1.pdf However, I'm wondering how often you could use this feature, adding the dial usually increases the OD of the movement, so you would need a new (larger) adapter ring tuned to the OD of the dial and I wouldn't like to grip the dial in any kind of movement holder if It could be avoided for fear of damaging it. Maybe I'm misunderstanding you?
    • Hi Frank, you have dived headlong into the deep end. Hairspring work has to be the scariest thing a newbie has to tackle. Your hairspring appears to be bent and just putting it back into the regulator would not allow the balance to work properly. It might start oscillating but the performance would not be good. The proper thing to do is to unstud the hairspring, remove the hairspring from the balance, reinstall the hairspring on the stud carrier, reshape the endcurve and centre the collet to the balance jewel hole. This challenge would either make you or break you. Hope that you will be able to fix your watch. Welcome to the world of watchmaking.  Watch this video. It think it'll give you an idea of the task ahead. From your 1st photo, I think you have a etachron type stud. Let me see if I can find a video on how to remove it from the arm.
    • Have read of the Tech Sheet attached on the balance section page 12. It may be bent but until you reposition it back in the regulator pins you'll never know. Cheers CJ 4R35B_4R36A.pdf
    • Aloha All, My Seiko 4R35B movement stopped working today. Upon closer inspection, it looks like the balance spring came out of the regulator pin. This is my first time working on a balance. Any advice on how to get this spring repositioned (back to normal)? I'm pretty sure that while adjusting the beat error on this movement, I must have turned the stud (I didn't even know they turned), and the spring eventually fell out.  Will the spring go back to even spacing when it's back in the pin, or does it look bent? Thanks, Frank  
×
×
  • Create New...