Hi guys, 

I working on a watch with small seconds, and the extended pivot on the fourth wheel is a bit bent. I would assess it to be maybe 3 or 4 degrees bent. This is enough for the seconds hand to rotate on a tilted plane, and the dial had been marked by it. 

Do you try to straighten the pivot, and if so, how? 

--

Thanks, 

Stian 

Link to comment
Share on other sites

Hi Stuart, 

Thanks, I should have specified that this is a vintage watch and finding a new arbor would be very difficult. 

Would you have any guidance on when you would expect it to break and when you would think you can straighten it? E.g would it depend on the angle, the method etc? 

Stian 

Link to comment
Share on other sites

Hi Stian,

It is more likely to break if you can't find a replacement :-)

On older watches, the hardness of these parts is somewhat unpredictable. Seitz makes a special tool for straightening pivots, but they are expensive even second hand.  This would give you more control, but wouldn't help with certainty.

If it is only a few degrees you may get away with it. Do you have a staking set with hollow punches?

If you post some pictures we may be able to help identify the movement. Key features are usually the keyless works parts and the diameter, but also good to see the bridges and any markings

 

Link to comment
Share on other sites

I had the same problem and was successful in straightening it out. I used a pair of pliers and carefully worked it. Then I used my Jacot tool to smooth out any scratches I made with the pliers. As mentioned by others, the pivot could break if you are not careful and even if you are. However, you really have no choice other than getting a new wheel and shaft.

Sent from my GT-N5110 using Tapatalk

Link to comment
Share on other sites

Never done it myself, but from what I heard, if you want to work with the pivot (in any way) you must first soften the material (meaning turning it red, letting it cool down) and then hardening it again.

Good luck with that!

 

 

Link to comment
Share on other sites

@ matabog: Oh god, do not heat to red! Light blue is sufficient.

If it is bent 3-4 deg only, danger of breaking is not so high. I do this very often, repairing chronographs. I use to hold the pivot (the straight part) in a lathe collet, turn the spindle and compare the other pivot to the tip of the headstock. Bend the pivot with light taps until the wheel wobbles no more.

Frank

 

 

 

Link to comment
Share on other sites

General answer.

1st step (hardening). Heat red hot and quench in oil.

2nd step (tempering). Heat but not red hot. straw is the usually quoted  colour , then quench again.

The problem is these processes work on larger items where the piece heats up gradually. A small part like a pivot will heat up red-hot practically instantly. You would need to set up a bed of copper shavings and heat this part on it but it pretty hit and miss. There are some good videos on hardening watch parts on youtube.

A replacement would be the way to go.

Anilv

 

Link to comment
Share on other sites

I came across this thread whilst researching re-pivoting earlier. http://mb.nawcc.org/showthread.php?118580-Escape-wheel-pivot-repair

The idea of letting down the temper slightly might appeal. I'm no expert in this, but suspect that re-tempering the whole pinion with wheel attached is going to cause you bigger issues than you have already.

Link to comment
Share on other sites

 

I came across this thread whilst researching re-pivoting earlier. http://mb.nawcc.org/showthread.php?118580-Escape-wheel-pivot-repair

The idea of letting down the temper slightly might appeal. I'm no expert in this, but suspect that re-tempering the whole pinion with wheel attached is going to cause you bigger issues than you have already.

You are right. I do not heat at all, but reducing the temper to blue or light blue may help. Tempering again is not needed.

Frank

Link to comment
Share on other sites



  • Recently Browsing

    • No registered users viewing this page.
  • Topics

  • Posts

    • These are all American movements (with the exception of the "Rubis"), and are all almost certainly "negative set" which means the stem is part of the case. So it's normal that they are all missing- they are with their cases. You will need male square bench keys to wind/disarm them. Vintagewatchstraps has a great writeup on the different systems. But basically, any American "x" size movement will fit any case for that size, possibly with some adjusting of the stem position. With Swiss movements, there is some interchangeability between calibers, usually within the same maker's range, but not really overall- there are thousands of different stems out there.
    • Hi, I'm very new to watchmaking and this is my first time posting here.  I've bought a lot of 10 vintage pocket watches size 0s from e-bay and just got them today.  Most of the balance wheels sprung quite freely and thus seemed like a worthy endeavor as a first batch for exploration.  I've just realized that none of them have any winding stems. Is there any way I could source appropriate winding stems for the movements? There seems to be assortments of various stems selling in bulk on aliexpress, but would any of them fit?  I've read on other threads that some people lathe their own stems (which is waaaay out of my current skill set, which is pretty much nil). Others say that you 'just have to try a few and see if they fit'. I would much appreciate any advice for this matter. Thanks!
    • Nice work.  In the last year, I have been servicing Accutron 218s.  I have the official Accutron hoder that provides electrical contact to the movement.  It is a pretty clever design.  There is a cut in the ring of the holder (shaped like a "C").  When in relaxed state, the holder is slightly smaller than the watch movement.  You spread the cut slightly and drop the movement in and release.  Very clean.  I have made 3D versions of this setup.  Have not explored using it generally for other movements.
    • Double Oooooo   Removal tool? Dreamed of one of these. However, Kalle on Chronoglide showed everyone my system with the pegwood. Worked a treat. Felt so chuffed to be mentioned. https://www.youtube.com/watch?v=tTFrXjiyGKc 46:40 for the wheel removal. Mentions me at 50:00 and does the removal with the pegwood. Felt like my 15 minutes of fame.  
    • Sirius. Thank you for helping others with that information. This is why this forum is so good.
×
×
  • Create New...