Lapping a Speedmaster MkII case


Recommended Posts

I have over the years refinished a few Speedmaster MkII cases for friends.

They are fun to work on as they are,usually quite beat up och the surfaces have been polished a few times to many.

Last week a friend of mine told me that there was a 1970 MkII for sale on a Swedish auction site. I was born 1970 so this watch I just had to have!

On Sunday when the auction was about to close the website where the auction was held started to act up and I could not log on.........
About thirty seconds before it closed the webpage loaded and I was able to submit my offer....then it was down again......did I win or not!!??,
I waited for the usual confirmation mail when you have won an object and five minutes later I had mail, -Yesssssss.....

The watch arrived On Tuesday and looked like this:

 

147138532608026000_resized.jpg 

147138532975095700_resized.jpg

147138532940169400_resized.jpg

Not to bad, but the sunburst was gone and the top surface had......"straight graining" .....I guess the previous owner used a abrasive rotating mop or something!

The case was practically free of deeper scratches and dings so a good prospect for a lapping session!

The case was stripped and I started with the sides:

147138609243966000_resized.jpg

I do this part in my small Boley lathe with 90mm discs that I have made and a small tiltable table to set the angle.

Depending on the geometry of the case you can either slide the case directly on the table or use a adaptor to get the right angle - in this case no adaptor was used.

First run on one side done:

147138609128220700_resized.jpg

First disc is 400P so you have to be careful, especially with the start/edge where the case can grip the disc - and you do NOT want this as you will have a case with scratches in places they where not intended to be!

After 400P I move up to 1000P and finally a last run with 2000P. This usually gets the surface almost up to mirror finish but,a quick final touch with a mop gives it,that final shine.

When the surfaces are flat and when needed polished, it is time to grain the sides and lapp the sunburstpattern on the top.

This is done in a small mill I have with a tiltable spindle using a 305mm rotating disc and another home made tiltable table.

For this case I use a 120P paper so you really have to take it slow and be sure all the angles are set up correct or the disc will chew material in places you do nor want it to!

The result

 

147138532738919200_resized.jpg

147138532704848100_resized.jpg

I was not 100% pleased! There where some spots there the graining did not go al the way up to the grained edge around the glass. This was obvious in the pictures and reflections in some angles on the wrist - I relapped to top surface....

147155095292512700_resized.jpg

147155095351387100_resized.jpg

Some grease from my fingers on the chamfer in the pictures but the graining is better now!

I am waiting for a NOS dial and crown - when they get here I will strip and clean the movement as well.

 

 

 

 

 

Edited by RCDesign
  • Like 8
Link to comment
Share on other sites

 

 

I have seen these lapping machines before, but I can not quite figure out how it works so that it forms this beautiful  sunburst pattern? Can you please show the principle of image , sketch, video , etc.

 

Very fine result by the way!!
Edited by maclerche
Link to comment
Share on other sites

the key to lapping is the diamond plate ( the disk in the photo).  granules are pressed into a metal disk.   mainly to be used on a lathe where you can control the speed. it is FM  [friggin magic].  used mainly by the Germans in WW11.

Link to comment
Share on other sites

On 2016-08-19 at 10:12 PM, maclerche said:

"I have seen these lapping machines before, but I can not quite figure out how it works so that it forms this beautiful  sunburst pattern? Can you please show the principle of image , sketch, video , etc."

Here is a simple picture of how it's done:

slipskiva-jpg.90909

The case is presented to disc at 270deg as close to the edge as possible and at the horizontal center using a tiltable table shown above. The case is rotated in this location using a specialy made holder/chuck and "viola" you have a sunburst pattern!


As the length of the case in contact with the disc is so short the brushing will be almost straight, but it will NOT be perfectly straight - that is the reason I want as big a disc as possible! 

 

For now I have settled for 305mm as this is the largest dimension I can get pappers for - easy!

I'm using standard paper right now but have a set of old cast iron discs that have been used by my grandfather to lapp using glue and a special absrasive mixture he had when lapping diamonds.

 

To use them I firs have to renovate the matching headstock of the lathe he used - but I think it will be woth while as that lathe will be a good base for a more advanced lappingmachine! :)

 

Here is a video of the principle for getting the pattern:

 

Sunburst lapping a Omega

 

I like to use a much lower rpm setting and use a fixture for the watch case - but thats just me!

 

Here is another machine

 

Edited by RCDesign
  • Like 3
Link to comment
Share on other sites

Another example to show it's the ingenuity and skills that make  the results, not the tool.

In theory the large disc could be replace by a drum with abrasive on the side, but I've never seen anybody doing that.

Link to comment
Share on other sites

Thank you very much for posting this, great work!

in the future I would love to be able to setup a lapping machine, as most of the watches I like have a sunburst finish, and it is really the only way to achieve clean edges.

are you the same person who posted on the TZ forum a while ago! I think I recognise the milling machine from somewhere! 

Do you think one could achieve a good setup with a lathe (provided it can take a 305mm grinding disc of course)? I have been thinking along those lines...

 

Link to comment
Share on other sites

My lapping attempts have been posted on other sites as well so it's probably my mill you have seen before!

Lapping can be done in many different ways but with a disc seams to be the easiest way!

I actually built a small machine from a belt sander where I can index my existing chuck to the right angle. This will produce 100% straight graining IF I can get hold of good sanding belts that have no overlap (where they are glued together to a circle) => same thickness all around!

A lathe is a good starting point for setting up a lapping rig but my mill actually has one big advantage - I can set x, y AND z (the height) This makes setting pup the tiltable table and chuck so much easier!

" Do you think one could achieve a good setup with a lathe (provided it can take a 305mm grinding disc of course)? I have been thinking along those lines... "

Do not get stuck with my 305mm discs - the commercial lappingmachines I have seen all have 240mm discs! A titable table on you cross slide and a suitable chuck or holder for the case and you are good to go! ;)

 

Simple chuck I used when I started testing different lapping setups:

144113122856684500_resized.jpg

Edited by RCDesign
  • Like 2
Link to comment
Share on other sites

The difference the proper finishing made is night and day, I love the look of this piece and I'm thinking the watch is lucky to have you for an owner. I still can't quite work out how you created the sunburst, despite the explanation, but then I've never used machinery like that. 

Link to comment
Share on other sites

On 2016-08-25 at 8:13 PM, Ishima said:

The difference the proper finishing made is night and day, I love the look of this piece and I'm thinking the watch is lucky to have you for an owner. I still can't quite work out how you created the sunburst, despite the explanation, but then I've never used machinery like that. 

If you look at this clip )abt. 40s in) you se how the sunbust lapp an Omega case! ;)

 

Nothing magical - you just have to have a sturdy setup and a good fixture to get the angle/s right!

  • Like 1
Link to comment
Share on other sites



  • Recently Browsing

    • No registered users viewing this page.
  • Topics

  • Posts

    • I voted leave too, my reasoning was the the EU is undemocratic, no elected officials. I don't regret it but I  am sad that both sides acted like petulant toddlers.  Shameful.  I'm not on other forums but if I was and left this site, would you shun me? Of course not, we aren't petulant toddlers.  
    • This is a type of tool that may be suitable to remove the bezel - though note that I'm pretty sure the watch should be face down - not face up, as in some of the photos of these tools on amazon & ebay! If you try one one of those, put the movement screws back in first to avoid accidents. https://www.amazon.co.uk/Removal-Professional-Remover-Watchmaker-Diameter/dp/B09XCH4QVN?source=ps-sl-shoppingads-lpcontext&ref_=fplfs&smid=A296NCMMFVXSDN&th=1  
    • Hi, I’m constantly asking my wife to help me with removing the stem in order to complete casing. To expand, this is not a challenge for me when the setting lever is secured by a screw (older calibers). However when the setting lever is attached to a spring loaded setting lever axel, like on more modern calibers, I simply don’t see how to apply enough pressure on the button to get the stem out short of putting the movement face down with the dial and hands attached, which I’m loath to do in order to avoid damaging the dial/hands? what technique should I be using? thanks  
    • Many thanks for your advice (being borne in mind at present) & offer Dell. When I was given the clock the plastic anchor was loose on the arbour (it had split at the 'hole') &, after repairing this, I have been trying to determine whether the spindle (pin) should be perpendicular when the pallet is sitting on a flat surface; or whether, when installed, its L-R extremes (or alternatively its tick & tock points) should lie at equal angles from the vertical when moved with spring absent. I can get the clock to run but in every such configuration the top block has to be turned anti-clockwise (from above) by quite a bit in order to be 'in beat' & it always runs fast (despite the pendulum being set to as slow as possible). This makes me wonder if there is any particular feature of/fault in a torsion spring clock which determines which turn direction (if any) is necessary to get it 'in beat'; & whether there would be a different set of settings that would get it running nearer to time at somewhere around the mid timing/inertia position which would then allow tweaking of the fast/slow setting.
    • Now this has happened I bet China or India just to name two will start to produce none genuine parts.  I did. But idiot Boris Johnson failed miserably in his negotiations. The E U stitched up the UK like a kipper. Nigel Farage  offered his help but big head Boris declined. So this is why we are in this mess all because Johnson wasn't clever enough.  
×
×